Foadian F, Soltanieh M, Adeli M, Etminanbakhsh M. THE FORMATION OF TiAl3 DURING HEAT TREATMENT IN EXPLOSIVELY WELDED Ti-Al MULTILAYERS. IJMSE 2014; 11 (4) :12-19
URL: http://ijmse.iust.ac.ir/article-1-716-en.html
Abstract:   (19694 Views)
Metallic-intermetallic laminate (MIL) composites are promising materials for structural applications especially in the aerospace industry. One of the interesting laminate composites is the Ti-TiAl 3 multilayer. In this work, commercially pure sheets of aluminum and titanium with almost equal thickness of around 0.5 mm were explosively joined. The achieved multilayers were annealed at 630 ℃in different times so that an intermetallic layer was formed at the Ti/Al interface. The resulting microstructure was studied by optical and scanning electron microscopy and Energy Dispersive Spectroscopy (EDS). TiAl3 was the only intermetallic phase that was observed in all annealing times. The kinetics of the formation of TiAl 3 was investigated and compared to previous research studies performed on Ti-Al multilayers which were fabricated using methods other than explosive welding.
Full-Text [PDF 5588 kb]   (5356 Downloads)    

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb