In this research accumulative roll bonding process as sever plastic deformation process was applied up to 8 cycles to produce the ultrafine grain copper. Microstructure of cycle 1, cycle 4 and cycle 8 investigated by TEM images. By analyzing TEM images the grain size measured below 100 nm in cycle 8 and it was with an average grain size of 200 nm. Corrosion resistance of rolled copper strips in comparing with unrolled copper strip was investigated in acidic (pH=2) 3.5 wt. % NaCl solution. Potentiodynamic polarization and EIS tests used for corrosion resistance investigations. The corrosion morphologies analyzed by FE-SEM microscopy after polarization test and immersion for 40 hours. Results show that the corrosion resistance decreased up to cycle 2 and increased after rolled for forth time. The corrosion degradation was more intergranular in cycle 2 and unrolled counterpart. It was more uniform rather than intergranular type in cycle 8. Corrosion current density in unrolled sample (2.55 µAcm -2 ) was about two times of that in cycle 8 (1.45 µAcm -2 ). The higher corrosion rate in cycle 2 in comparison with others was attributed to unstable microstructure and increase in dislocation density whereas the uniform corrosion in cycle 8 was due to stable UFG formation

Keywords: Ultrafine Grain, Corrosion, Copper, NaCl, Accumulative Roll Bonding, SPD

Full-Text [PDF 6652 kb]   (5166 Downloads)    

Add your comments about this article : Your username or Email:

---

---