Abdulkhadar U M, Shivakumar Gouda P S, Shirahatti A, Veeresh Kumar G B, Banapurmath N R. Effect of Ply Orientation on Residual Stresses and Their Influence on Mode I Fracture Toughness of Glass-Epoxy Composites with 0°//0° Crack Interface. IJMSE 2021; 18 (4) :1-10
URL: http://ijmse.iust.ac.ir/article-1-2368-en.html
Abstract:   (6065 Views)
The energy release rate for delamination in a laminated composite is supposed to be the material property being considered as independent of non-material property variables. However, Mode I fracture toughness(GI) is found to vary with lamina arrangement, geometrical dimensions, and process-induced stresses.  In this investigation, the influence of lamina stacking arrangement on process-induced stresses and their effects on GI of laminated composites are studied. Unidirectional (UD) ([0]16) and cross-ply ([902/06]s, [904/04]s and [906/02]s) Glass/ epoxy (GE) composites with the delamination plane at 0◦//0◦ were prepared by manual layup method and post-cured at 120 °C for 4 hours. GI of composite laminates were experimentally determined using a double cantilever beam(DCB) specimen as per ASTM D 5528. The slitting method was applied to determine the Process-induced stresses in GE laminates. The stacking sequence of laminas was found to have a noticeable effect on the state of residual stresses and GI of GE laminates. Residual stresses do not have much influence on the GI for delamination initiation, whereas GI  for the crack propagation was found to increase with a gradual increase in compressive residual stresses in GE laminates.
Full-Text [PDF 874 kb]   (4873 Downloads)    
Type of Study: Research Paper | Subject: Ceramics

Add your comments about this article : Your username or Email:

Send email to the article author

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb