Hadi M, Bayat O, Karimi H, Sadeghi M, Isfahani T. Effect of Solution Treatment on the Rollability of a Cu-Ni-Mn-Sn Alloy. IJMSE 2022; 19 (1) :1-11
URL: http://ijmse.iust.ac.ir/article-1-2266-en.html
Abstract:   (5537 Views)
In this research, the effect of initial microstructure and solution treatment on rollability and crystallographic texture of a Cu-Mn-Ni-Sn alloy has been investigated. The initial tests indicated that the rolling of the alloy at different temperature conditions is not possible due to formation of second phases. Herein to eliminate the segregated phases, according to DTA analysis, proper temperature for solution treatment was selected as 750°C applied at different periods of time. The obtained results showed that after 15-hour solution treatment, the complete elimination of Sn, Mn, Ni, and Fe-rich phases can be achieved. Also, the peaks of XRD shifted to the higher angles indicating that the alloying elements are dissolved. Meanwhile, the intensity of the texture reduced and the dominant texture changed from Goss and Brass-texture to Copper-texture. Accordingly, the amount of maximum total reduction at the rolling process increased from 16.37 to 109.46 after solution treatment.
Full-Text [PDF 3031 kb]   (2550 Downloads)    
Type of Study: Research Paper | Subject: Ceramics

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb