Confined and unconfined crystallizations of poly(3-hexylthiophene) (P3HT) were studied in the solution-grown supramolecules and melt-grown systems using a differential scanning calorimeter. The carbon nanotube (CNT) and reduced graphene oxide (rGO) and their functionalized (CNT-f-COOTh and rGO-f-TAA) and grafted (CNT-g-PDDT and rGO-g-PDDT) derivatives were employed to develop the samples. The absorbance, structure details via Scherrer formula, fusion enthalpy (ΔHm) and crystallinity (Xc) were measured in two distinct confined/unconfined crystallization environments. Although the functionalized-CNT/rGO precursors partially reduced the crystallite qualities with respect to the pristine CNT and rGO ones in the solution-grown supramolecules, they did not affect the structural properties in the melt-grown samples. Grafted carbonic materials could be considered as appropriate seeds for the arrangement of P3HTs in both solution and melt crystallizations. The best absorbances, larger and more compact crystals, and higher melting point, ΔHm, and Xc values were recorded for the pre-developed CNT-g-PDDT/P3HT stem-leaf (6.09–22.51 nm, 3.52–13.89 Å, 239.8 °C, 30.86 J/g and 83.40%) and rGO-g-PDDT/P3HT coarse-patched (5.96–20.76 nm, 3.57–13.95 Å, 237.6 °C, 29.13 J/g and 78.73%) supramolecules. Although the melt-grown CNT-g-PDDT/P3HT (201.4 °C, 215.3 °C, 16.22 J/g and 43.84%) and rGO-g-PDDT/P3HT (205.4 °C, 218.8 °C, 18.06 J/g and 48.81%) nanostructures were not as perfect as the respective solution-grown nano-hybrids, they were well-arranged with respect to the CNT/P3HT, CNT-f-COOTh/P3HT, rGO/P3HT and rGO-f-TAA/P3HT samples
Full-Text [PDF 1584 kb]
(5914 Downloads)
1) Confined/unconfined crystallizations of P3HT/carbonic materials were investigated in DSC-crystallized nanostructures and solution-grown supramolecules.
2) Absorbance, structure details, fusion enthalpy and crystallinity were focused in two different crystallization environments.
3) The best results were recorded for CNT-g-PDDT/P3HT stem-leaf and rGO-g-PDDT/P3HT coarse-patched supramolecules.