Tajer Kajinebaf V, Zarrin Khame-Forosh M, Sarpoolaky H. Preparation and Characterization of Nanostructured Titania-coated Silica Microsphere Membranes with Simultaneous Photo-catalytic and Separation Applications for Water Treatment. IJMSE 2020; 17 (1) :35-44
URL: http://ijmse.iust.ac.ir/article-1-1149-en.html
Abstract:   (17871 Views)
In this research, the nanostructured titania-coated silica microsphere (NTCSM) membrane consisting of titania-silica core-shell particles on α–alumina substrate was prepared by dip-coating method. The silica microspheres were synthesized by the Stöber method, and the nanostructured titania shell was obtained from a polymeric sol. Then, the prepared core-shell particles were deposited on alumina substrates. The samples were characterized by DLS, TG-DTA, XRD, FTIR and SEM. The photo-catalytic activity of the NTCSM membranes was evaluated using photo-degradation of methyl orange solution by UV–visible spectrophotometer. Also, physical separation capability was investigated by filtration experiment based on methyl orange removal from aqueous solution using a membrane setup. The mean particle size distribution of silica microspheres was determined to be about 650 nm that by deposition of titania nano-particles increased up to about 800 nm. After 60 min UV-irradiation, the dye removal efficiency was determined to be 80% by the membrane. By coupling separation process with photo-catalytic technique, the removal efficiency was improved up to 97%. Thus, the NTCSM membranes showed simultaneous photo-degradation and separation capabilities for dye removal from water.
 
Full-Text [PDF 940 kb]   (4036 Downloads)    
Type of Study: Research Paper | Subject: Ceramics

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb