Salehtash F, Banna Motejadded Emrooz H, Jalaly M. An Investigation on the Adsorption Behavior of a Mesoporous Silica Synthesized by a Surfactant-assisted Method in an Acidic Media. IJMSE 2018; 15 (2) :48-56
URL:
http://ijmse.iust.ac.ir/article-1-1035-en.html
Abstract: (19044 Views)
Mesoporous SiO2 nanopowder was synthesized under an acidic condition by a sol-gel method using various amounts of cetyltrimethyl ammonium bromide (CTAB) as structure directing agent. The samples were investigated with XRD, SEM, FTIR, TEM and N2 absorption-desorption analysis. Also, the incremental effect of surfactant were examined. The results obtained from the analysis suggested that an increase in the amount of surfactant resulted in increasing specific surface area, pore size and pore volume, of the synthesized particles up to 549 m2.g-1, 17.3 nm, and 2 cm3.g-1, respectively. Absorption behavior of the mesoporous silica was investigated for degradation of methylene blue pigments (MB) in aqueous solutions. The samples SC0, SC0.5 and SC1 showed the maximum absorption capacities of 333, 454 and 526 mg/g, respectively
Full-Text [PDF 4118 kb]
(4092 Downloads)
- Mesoporous silicon oxide was synthesized by a sol-gel method.
- Cationic CTAB was used as the directing agent.
- The values of ~4–17 nm and ~314–548 m2g-1 were obtained for pore sizes and surface areas of the samples with different CTAB amounts.
Type of Study:
Research Paper |
Subject:
Ceramics