Torkamani H, Rashvand H, Raygan S, Rassizadehghani J, Palizdar Y, Garcia Mateo C et al . EFFECTS OF MO ADDITION ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF CAST MICROALLOYED STEEL. IJMSE. 2017; 14 (3) :76-85
URL: http://ijmse.iust.ac.ir/article-1-928-en.html

Abstract:   (274 Views)

In industry, the cost of production is an important factor and it is preferred to use conventional and low cost procedures for producing the parts. Heat treatment cycles and alloying additions are the key factors affecting the microstructure and mechanical properties of the cast steels. In this study an attempt was made to evaluate the influence of minor Mo addition on the microstructure and mechanical properties of conventionally heat treated cast micro-alloyed steels. The results of Jominy and dilatometry tests and also microstructural examinations revealed that Mo could effectively increase the hardenability of the investigated steel and change the microstructure features of the air-cooled samples. Acicular microstructure was the consequence of increasing the hardenability in Mo-added steel. Besides, it was found that Mo could greatly affect the isothermal bainitic transformation and higher fraction of martensite after cooling (from isothermal temperature) was due to the Mo addition. The results of impact test indicated that the microstructure obtained in air-cooled Mo-added steel led to better impact toughness (28J) in comparison with the base steel (23J). Moreover, Mo-added steel possessed higher hardness (291HV), yield (524MPa) and tensile (1108MPa) strengths compared to the base one.

Full-Text [PDF 7443 kb]   (57 Downloads)    

Add your comments about this article : Your username or email:
Write the security code in the box

Send email to the article author


© 2016 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb