Manafi S, Joughehdoust S. Effect of Heat Treatment on Formation of Calcium Titanate Hollow-Crystals Nanostructures Prepared by Hydrothermal Method. IJMSE 2020; 17 (2) :1-7
URL: http://ijmse.iust.ac.ir/article-1-1322-en.html
Abstract:   (13720 Views)
In this research, calcium titanate (CaTiO3) hollow crystals have been successfully prepared via hydrothermal method. Titanium tetrachloride, calcium chloride dihydrate and potassium hydroxide were used as Ti, Ca and precipitating agent, respectively. The hydrothermal synthesis was performed at different temperatures and time durations. The negative amount of the Gibbs free energy shows the reactivity of the reaction at room temperature. Characterization of CaTiO3 was carried out using scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM) and X-ray diffraction (XRD). The optimum condition for preparing CaTiO3 is the sample kept in an autoclave at 300 ℃ for 3 h that requires less energy and time which consists of a high degree of crystallinity. In this research, tetragonal CaTiO3 hollow crystals have been successfully prepared via hydrothermal method. TiCl4, CaCl2.2H2O, and KOH were used as Ti, Ca and precipitating agent, respectively. The hydrothermal synthesis was performed at different temperatures and time durations. Characterization of CaTiO3 was carried out using SEM, HRTEM, and XRD. The sample kept in the autoclave at 300 ℃ for 3 h well crystallized and required less energy and time for synthesis. The powder has a homogenous dispersity of crystals with the range of nanometer to micrometer sizes which makes it a good candidate as a photocatalyst material
Full-Text [PDF 1332 kb]   (7155 Downloads)    
Type of Study: Research Paper | Subject: Ceramics

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb