K. Ghadarghadr Jahromi, , A. Zarei-Hanzaki, O. Golmahalleh. ULTRA FINE FERRITE FORMATION IN Si-Mn TRIP STEELS. IJMSE 2008; 5 (1) :1-7
URL: http://ijmse.iust.ac.ir/article-1-124-en.html
Abstract:   (31914 Views)
Abstract: In the present investigation, the effects of thermomechanical processing parameters and the steel chemical composition on the ultra fine ferrite formation characteristics were studied. This was programmed relying on the capabilities of strain induced transformation (SIT) phenomenon and applying to different grades of Si-Mn TRIP (Transformation Induced Plasticity) steels. Accordingly, wedge shaped specimens were rolled at two different temperatures, above and below the austenite-to-ferrite transformation temperature (Ar3). An ultra fine ferrite grain size, in the scale of some hundred nanometers, was obtained by rolling the specimens with lower Si content at a temperature below the related Ar3 temperature. The amount of reduction, which was resulted in the latter microstructure, was realized to be about 55%.
     
Type of Study: Research Paper |

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb