Kaiser M S. FRACTIONAL RECRYSTALLIZATION KINETICS IN DIRECTLY COLD ROLLED Al-Mg, Al-Mg-Sc AND Al-Mg-Sc-Zr ALLOY. IJMSE. 2014; 11 (4) :80-87
URL: http://ijmse.iust.ac.ir/article-1-725-en.html

Abstract:   (1790 Views)
The evaluation of texture as a function of recrystallization has been characterized for directly cold rolled Al-6Mg, Al-6Mg-0.4Sc and Al-6Mg-0.4Sc-0.2Zr alloys. Samples were annealed isothermally at 400 °C for 1 to 240 minutes to allow recrystallization. Recrystallization kinetics of the alloys is analyzed from the micro-hardness variation. Isothermally annealed samples of aluminum alloys were also studied using JMAK type analysis to see if there exists any correlation between the methods. Recrystallization fraction behavior between two methods the scandium added alloys show the higher variation due to precipitation hardening and higher recrystallization behavior. The scandium and zirconium as a combined shows the more variation due to formation of Al3(Sc, Zr) precipitate. From the microstructure it is also observed that the base Al-Mg alloy attained almost fully re-crystallized state after annealing at 400 °C for 60 minutes
Full-Text [PDF 5935 kb]   (1122 Downloads)    

Add your comments about this article : Your username or email:
Write the security code in the box

Send email to the article author


© 2016 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb