materials can be fabricated by sintering of W-Cu composite powders. In this research W-20%wt Cu composite powders

was synthesized via a co-precipitation method. Precipitate obtained from a mixture of copper nitrate and ammonium

paratungstate (APT) in distilled water contained W-Cu compounds. This precipitate was washed, dried and calcined

at 550

of dried precipitate powder was determined by thermogravimetry (TG), differential thermal analysis (DTA) and X-ray

diffraction (XRD). The sintering of the reduced powders was investigated as a function of temperature. Relative density

of more than 98% obtained for the powders sintered at 1200

close to theoretical calculations. The hardness of the sintered powders was 320 Vickers.

W-Cu composites are widely used as contacts, heat sinks and electro discharge electrodes. These kinds of°C in air and then reduced in H2 atmosphere in order to convert to W-Cu powders. The calcination temperature°C . The corresponding electrical conductivity was too
     