Volume 15, Issue 2 (June 2018)                   IJMSE 2018, 15(2): 1-13 | Back to browse issues page

XML Print

Abstract:   (1305 Views)
In the current work, the properties of cement pastes doped with high amounts of ground granulated blast-furnace slag (HVS) were investigated. Portland cement (PC) was substituted with ground granulated blast-furnace slag (donated as slag) at very high amounts of 85%, 90%, 95% and 100%, by weight. PC paste without any content of slag was used as a reference. Some fresh and hardened properties such as workability, density, compressive strength up to 56 days, pH value and drying shrinkage up to 200 days were measured. The various phases formed were identified using X-ray diffraction (XRD) and thermogravimetric analysis (TGA). The microstructure of the formed hydration products was determined by scanning electron microscopy (SEM). The results indicated that HVS has higher workability and higher drying shrinkage beyond 60 days. On the other hand, HVS has lower pH, density and compressive strength.
Full-Text [PDF 6385 kb]   (366 Downloads)