Abstract: (14221 Views)
In this work, the different fuels (citric acid, glycine and urea) were used for solution combustion synthesis of CoFe2O4 powders. X-ray diffraction, Raman spectroscopy, electron microscopy and vibrating sample magnetometry techniques were employed for characterization of phase evolution, cation distribution, microstructure and magnetic properties of the as-combusted CoFe2O4 powders. Single phase CoFe2O4 powders with partially inverse structure in which the Co2+ cations are distributed in both tetrahedral and octahedral sites were synthesized by the citric acid, glycine and urea fuels. The as-combusted CoFe2O4 powders by the citric acid fuel exhibited the highest inversion coefficient. The crystallite size of the as-combusted CoFe2O4 powders synthesized by urea fuel was 15 nm, increased to 41 and 52 nm for the glycine and citric acid fuels, respectively. Furthermore, the solution combusted CoFe2O4 powders showed ferromagnetic behavior with saturation magnetization of 61.9, 63.6 and 41.6 emu/g for the citric acid, glycine and urea fuels, respectively. The high crystallinity and particle size of the as-combusted CoFe2O4 powders using glycine fuel led to the highest magnetization and the moderate coercivity.
Full-Text [PDF 5523 kb]
(3844 Downloads)
-Single phase CoFe2O4 powders were obtained using citric acid, glycine and urea fuels.
-Cation distributions were dependent on fuel type.
-The highest inversion coefficient was achieved using citric acid fuel.
-The fuel type through crystallite size and cation distribution influences on magnetic properties